Anti-friction solid-film coating based on molybdenum disulfide and graphite
It is used in sliding bearings in pumps and valves, plunger pairs of hydraulic equipment; sliding valves and ordinary valves in distribution, and control devices; gearwheels of power gears in the energy industry; inner-combustion engine parts including pistons and sliding bearings operated under extreme conditionse sliding valves and plain valves in distribution and control devices, in the gearwheels in power gears in Energy, in the parts of inner-combustion engines (including pistons, bearings, cams) operated under extreme conditions
Package sizes:
MODENGY 1006 in action
Before
After
MODENGY 1006 coating is successfully used on the calibrators' plates of the machine tools on producing honeycomb polycarbonate. A thin layer of this coating improves sliding of the sheets of the items along the plates preventing them from stick-slip motion.
Before
After
MODENGY 1006 coating based on molybdenum disulfide and graphite is used to extend service lifetime of the energy equipment parts operating under extreme conditions. It reduces friction and wear of the titanic bearings, and steel thrusts, provides trouble-free operating of the important units.
Before
After
In order to extend service lifetime of the dry gas seals, MODENGY 1006 anti-friction solid-film coating based on molybdenum disulfide and graphite is applied onto the ring surfaces facing each other. This reduces friction between the contacting surfaces decreasing parts wear, and eliminating excessive noise while the superchargers are operating.
Before
After
In order to reduce wear, and to extend service lifetime, MODENGY 1006 anti-friction solid-film coating based on molybdenum disulfide and graphite is applied onto working surfaces of diesel generators inserts.
Before
After
MODENGY 1006, and MODENGY 1066 reduce friction at the moments of starting and stopping as well as extend service lifetime of the highly loaded thrust bearings.
Before
After
In order to prevent scuffing of the parts, MODENGY 1006 and MODENGY 1009 anti-friction solid-film coatings are used. They reduce friction in rotation process of the cuff, and thus prolong service lifetime, and operation reliability of the unit.
Before
After
To extend service lifetime and reliability of the tappets operating, MODENGY 1006 anti-friction solid-film coating based on molybdenum disulfide and graphite is used. It is applied onto the supporting portion the parts, and contributes to reducing friction and wear.
Before
After
In order to extend service lifetime of the unit at operating under conditions of being exposed to the inert gas, the titanium bearing rings get applied with MODENGY 1006 based on molybdenum disulfide and graphite, and MODENGY 2560 based on tungsten disulfide and graphite coatings.
Before
After
The purpose is – to provide constant friction coefficient in steel/ Kevlar pair, corrosion protection, and to improve equipment reliability
Before
After
The coatings are applied onto the piston skirts of the compressors, diesel locomotives, and specialty machinery. These coatings protect the parts against increased friction, scuffing forming, and intensive wear at the moments of start, at so called ‘oil starvation’, at overloads which increases service life of the equipment, contributes to reducing noise and fuel consumption.
The coatings operate within a wide temperature range, have high load-carrying capacity, none fuel, oil, or solvent types destroy them.
The coatings operate within a wide temperature range, have high load-carrying capacity, none fuel, oil, or solvent types destroy them.
Before
After
MODENGY 1006 and MODENGY 1066 with low friction coefficient and high heat resistance are applied onto the calibrators to prevent forming defects on the polymer film surface.
Use of these coatings increases equipment efficiency, lowers defective product percentage, and significantly reduces risk of calibrator failure.
Use of these coatings increases equipment efficiency, lowers defective product percentage, and significantly reduces risk of calibrator failure.
Before
After
MODENGY 1006 and MODENGY 1014 increases tightness of the hydro-cylinders by forming a separating layer resistant to hydraulic oils. These coatings prevents stick-slip motion, reduces the friction losses as much as possible, and significantly extends service life of the equipment.
Additional expendable materials
and equipment
- MODENGY Special Cleaner-Activator is intended to clean, degrease, and activate surfaces
- MODENGY 1015 Special Solvent is intended to rinse equipment after the coating is applied and the uncured coating is removed
- MODENGY 1013 Special Solvent to control completeness of coating polymerization
- MODENGY M1-250 Spray gun - to apply MODENGY anti-friction solid-film coatings
Advantages
- Low friction coefficient
- High load carrying capacity
- Wide service temperature range
- Workability in dusty environment
- High adhesion
- High wear resistance at dynamic loads
- It has properties of anti-emergency lubrication
- Non-toxic after complete cure
- It prevents stick-slip motion
- Long service life (dependent on the unit construction – durable lubrication)
- It speeds up parts assembly with robots
Specifications
- Colour: grey-black
- Service temperatures range: -70 … +315 °C (for short times up to +450 °C)
- Standard coating consumption: 67 g / m²
- Cure temperature / time: +200 °С / 20 min
It is used in the following typical units
Sliding bearings, sliding guideways, gearings, cylinder-and-piston group, splined joints, and keyed connections, the other units with metal/metal friction pairs